High-toughness cobalt-based alloy and engine valve coated with same

ABSTRACT

A surface hardening material being excellent in impact resistance and having abrasion resistance is provided. Provided are: a high-toughness cobalt-based alloy containing 25.0 to 40.0 mass % of Cr, 0.5 to 12.0 mass % of a sum of W and/or Mo, 0.8 to 5.5 mass % of Si, and 0.5 to 2.5 mass % of B, 8.0 mass % or less of each of Fe, Ni, Mn, and Cu, and 0.3 mass % or less of C, the sum amount of Fe, Ni, Mn, and C being 10.0 mass % or less, and the remainder comprising 48.0 to 68.0 mass % of Co and unavoidable impurities; and an engine valve coated with the same.

TECHNICAL FIELD

The present invention relates to a surface hardening material used in various construction processes such as PTA powder overlay welding, TIG overlay welding, and thermal spraying, and more particularly to a high-toughness cobalt-based alloy used in a member that demands an impact resistance and to an engine valve coateded with the same.

BACKGROUND ART

Conventionally, in an engine valve, a Co—Cr—W—C type material represented by Stellite (registered trademark) (including patent documents 1, 2) and a Co—Mo—Si type material represented by Tribaloy (registered trademark) (including patent documents 3 to 7) are used, and particularly Stellite is used in a member that demands an impact resistance.

The Co—Cr—W—C type material has an insufficient abrasion resistance though having a high toughness as a surface hardening material, so that the material cannot withstand use for a long period of time. Also, the Co—Mo—Si type material has an insufficient impact resistance though having a high abrasion resistance as a surface hardening material, so that problems such as cracks and exfoliation accompanied thereby are raised.

PRIOR ART DOCUMENTS Patent Documents

-   Patent Document 1: JP-A-2001-123238 -   Patent Document 2: JP-A-2008-522039 -   Patent Document 3: Japanese Patent No. 4463763 -   Patent Document 4: JP-A-05-131289 -   Patent Document 5: JP-A-09-296241 -   Patent Document 6: JP-A-07-278780 -   Patent Document 7: JP-A-04-107235

DISCLOSURE OF THE INVENTION Problems to be Solved by the Invention

Surface hardening aiming at abrasion resistance or impact resistance is currently used widely in various fields of industry. However, due to an improvement in recent years in the consciousness to the environment, there is an increasing severity in the environment for use of industrial apparatus. In accompaniment therewith, a surface hardening material is requested to have a higher performance. In particular, in a filling material used in an engine valve, development of a surface hardening material being excellent in impact resistance and having abrasion resistance is demanded.

Means for Solving the Problems

In the present invention, in a study of an alloy composition for developing a surface hardening material excellent in impact resistance, the following target values have been set, and the conditions have been set to satisfy all of these.

(Target Value)

(1) Charpy impact value→10 J/cm² or more (2) Hardness→48 HRC or more (3) Overlaying workability→the fluidity of a molten pool formed at the time of overlay welding is good (4) Thermal impact value→cracks or exfoliation is not generated until 700° C.

In other words, a high-toughness cobalt-based alloy of the present invention that satisfies the above targets (1) to (4) contains 25.0 to 40.0 mass % of Cr, 0.5 to 12.0 mass % of a sum of W and/or Mo, 0.8 to 5.5 mass % of Si, and 0.5 to 2.5 mass % of B, wherein the remainder comprises 48.0 to 68.0 mass % of Co and unavoidable impurities. Here, the unavoidable impurities are impurities that are mingled unavoidably in the steps of producing each material and the like, though not intentionally added. Such impurities include, for example, Mg, S, O, N, V, Zr, Sn, and the like, and the total sum of these is typically 0.3 mass % or less, which is of a degree that does not affect the function of the present invention.

Also, a high-toughness cobalt-based alloy of the present invention contains 25.0 to 40.0 mass % of Cr, 0.5 to 12.0 mass % of a sum of W and/or Mo, 0.8 to 5.5 mass % of Si, and 0.5 to 2.5 mass % of B, and further contains 8.0 mass % or less of each of Fe, Ni, Mn, and 0.3 mass % or less of C, wherein the sum amount of Fe, Ni, Mn, Cu, and C is 10.0 mass % or less, and the remainder comprises 48.0 to 58.0 mass % of Co and unavoidable impurities.

Also, an engine valve of the present invention is filled or coated with a high-toughness cobalt-based alloy having the aforesaid composition. A more preferable engine valve is such that at least a face surface abutting against a sheet is filled or coated with the aforesaid high-toughness cobalt-based alloy.

Next, the reason why the range of each component of the high-toughness cobalt-based alloy pertaining to the present invention alloy is limited will be described.

Cr imparts abrasion resistance, impact resistance, corrosion resistance, and oxidation resistance by being dissolved into a Co solid solution which serves as a substrate (matrix). Also, part of Cr forms an intermetallic compound with B so as to be dispersed in the matrix, thereby further contributing to improvement in the abrasion resistance. However, when the content is less than 25.0 mass, sufficient abrasion resistance, corrosion resistance, and oxidation resistance cannot be obtained. When the content exceeds 40.0 mass %, the intermetallic compound is formed in a large amount in the metal tissue, thereby greatly lowering the toughness. Therefore, the range has been set to be 25.0 to 40.0 mass %.

Mo and W impart abrasion resistance and impact resistance by being dissolved into a Co solid solution, and part thereof forms an intermetallic compound with B, thereby further contributing to improvement in the abrasion resistance. However, when the sum of Mo and W is less than 0.5 mass %, the solid solution reinforcement is insufficient. When the content exceeds 12.0 mass %, the intermetallic compound is formed in a large amount, thereby greatly lowering the toughness (impact resistance). For this reason, the sum of Mo and/or W has been set to be within a range of 0.5 to 12.0 mass %.

Si cleans the molten metal and improves the fluidity at the time of filling by being dissolved into a Co solid solution and compositely added together with B, thereby improving the construction workability such as PTA, TIG overlaying, or thermal spraying. However, when the content is less than 0.8 mass %, it does not contribute to solid solution reinforcement, and moreover, the function of cleaning the molten metal will be insufficient. Also, when the content exceeds 5.5 mass %, an intermetallic compound is formed, thereby greatly lowering the toughness (impact resistance). For this reason, the content of Si has been set to be within a range of 0.8 to 5.5 mass %.

B imparts abrasion resistance by forming an intermetallic compound with Cr or Mo, and cleans the molten metal to improve the fluidity at the time of filling, thereby improving the construction workability such as PTA, TIG overlaying, or thermal spraying. However, when the content is less than 0.5 mass %, a sufficient amount of intermetallic compound is not formed, so that the abrasion property is lowered, and moreover, the function of cleaning the molten metal is insufficient. On the other hand, when the content exceeds 2.5 mass %, the intermetallic compound is large in amount, thereby greatly lowering the toughness (impact resistance). For this reason, the content of B has been set to be within a range of 0.5 to 2.5 mass %.

The cobalt-based alloy of the present invention can further contain 8.0 mass % or less of each of Fe, Ni, Mn, and Cu, and 0.3 mass % or less of C as added elements that do not give adverse effects on the physical properties. However, in order not to deteriorate the impact resistance and abrasion resistance, the upper limit value of the sum amount of Fe, Ni, Mn, Cu, and C has been set to be 10.0 mass % or less.

Effect of the Invention

The cobalt-based alloy of the present invention has characteristics of a Charpy impact value of 10 J/cm² or more and a hardness of 48 HRC or more, has a good PTA overlaying workability, and does not generate cracks or exfoliation until 700° C. in a thermal impact test of an overlay test piece, so that the alloy can be applied to a wide range of use as a surface hardening material having excellent impact resistance and abrasion resistance.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic view in one example of an engine valve coated with a high-toughness cobalt-based alloy of the present invention.

MODE FOR CARRYING OUT THE INVENTION

The cobalt-based alloy of the present invention can be obtained by heating and melting an ingot, in which Co as a base, Cr, Mo, W, B, and Si as added components, and Fe, Ni, Mn, Cu, and C added in accordance with the needs are each adjusted and blended to have a predetermined mass %, in a crucible within a melting furnace so as to form an alloy in a liquid form, and thereafter transforming the molten alloy into a powder by the atomization method or the melt-crushing method or casting in a predetermined mold to form a rod shape or a plate shape.

In particular, the cobalt-based alloy powder produced by the atomization method can be applied to surface reforming construction such as PTA overlaying or thermal spraying by being adjusted to have a particle size suitable for the intended construction method. The overlay-welded rod produced by the continuous casting method can be applied to surface reforming construction such as gas overlaying. Also, by constructing this powder or rod material on a face surface of an engine valve having various material qualities, an abrasion resistance can be imparted to the engine valve.

EXAMPLES

The alloys of the Examples of the present invention prepared and blended in the above-described manner and the alloys of the Comparative Examples were melted and subjected to measurement of the Charpy impact value and the Rockwell hardness by the methods described below. Also, an overlaying test and a thermal impact test were carried out by the methods described below.

(1) Charpy Impact Test;

By using an electric furnace, 100 g of an ingot having a blending composition of each alloy was heated to about 1600° C. and melted in a stream of argon, and was cast into a shell mold to be mechanically processed into a test piece (without a notch) described in JIS Z 2242:2005. Then, by using a Charpy impact tester, an impact test was carried out in accordance with JIS Z 2242:2005, so as to measure the impact value.

(2) Hardness Measurement;

A cast piece melted by the same method as described in the above (1) was mechanically processed into a shape of 10×10×20 mm to expose a parallel surface, and the top part of the parallel surface was subjected to wet polishing with a water-resistant abrasive paper of No. 240, so as to carry out a Rockwell hardness test in accordance with JIS Z 2245:2005. Here, the measurement was carried out in C scale.

(3) PTA Overlaying Test;

By using a high-frequency melting furnace, 100 kg of an ingot having a blending composition of each alloy was heated to about 1600° C. and melted in a stream of argon, and was pulverized by the gas atomization method, so as to adjust the particle size to 80 to 350 mesh by a vibration sieve. This alloy powder was subjected to plasma powder overlay welding on a face surface (the part shown by the reference sign 2 in FIG. 1) of an engine valve (umbrella diameter of about 70 mm, axial diameter of about 14 mm, and a total length of about 300 mm) fabricated by using a heat-resistant steel (SUH3) defined in JIS G 4311:1991, and the fluidity state of the molten pool formed at the time of overlay welding was examined. Here, the evaluation standard for the fluidity state is represented by any one of the following, and an alloy providing a good fluidity state is expressed as “Extremely good” or “Good”.

(Evaluation Standard)

Extremely good: equivalent to or more than Comparative Examples P, Q (cobalt self-fluxing alloy)

Good: equivalent to or more than Comparative Example A (Stellite 6)

Slightly poor: poorer than Comparative Example A but better than Comparative Example F (Tribaloy 400)

Poor: equivalent to or less than Comparative Example F

(4) Thermal Impact Test;

The engine valve fabricated by the same method as described in the above (3) was thermally treated for one hour in an electric furnace set at 400° C., and thereafter out into water of about 20° C. for quick quenching. Subsequently, the thermal treatment temperature is further raised by 50° C., so as to perform a thermal treatment for one hour and quenching with water. This is repeated until the thermal treatment temperature becomes 700° C., and whether cracks or exfoliation was generated or not after the thermal treatment at 700° C. was examined.

Table 1 shows the Examples of the present invention, and Table 2 and Table 3 show the Comparative Examples.

TABLE 1 Thermal impact test Impact (700° C.→quenching with water) Composition (mass %) value Hardness Overlay workability Presence or absence of No. Co Cr B Si W Mo Others J/cm² HRC State of molten pool cracks or exfoliation Alloys 1 67.5 25.5 1.0 5.2 0.8 — — 11 51.5 Good none of the 2 52.5 39.0 1.5 1.0 3.0 3.0 — 17 50.1 Extremely good none present 3 65.2 28.0 2.3 1.5 — 3.0 — 10 52.4 Extremely good none invention 4 55.5 30.0 1.5 2.0 5.5 5.5 — 10 50.8 Extremely good none 5 59.3 33.0 0.7 4.0 1.5 1.5 — 21 49.3 Good none 6 56.7 35.0 1.5 1.8 5.0 — — 16 49.3 Extremely good none 7 56.9 35.0 1.5 1.6 — 5.0 — 11 49.0 Extremely good none 8 58.8 30.0 1.2 4.0 6.0 — — 12 48.3 Good none 9 60.1 35.0 1.8 1.6 0 1.5 — 14 49.2 Extremely good none 10 61.9 27.0 1.7 2.4 5.0 2.0 — 12 51.3 Extremely good none 11 49.5 30.0 1.5 2.0 4.0 6.0 7Fe 11 49.7 Extremely good none 12 54.5 30.0 1.5 2.0 5.0 — 7Mn 17 48.3 Extremely good none 13 48.5 34.0 1.0 3.5 2.0 2.0 4.5Ni, 4.5Cu 12 50.6 Good none 14 57.2 35.0 1.3 2.3 4.0 — 0.2C 14 49.3 Extremely good none 15 48.3 38.0 1.5 2.0 5.0 — 5Mn, 0.2C 10 52.2 Extremely good none 16 57.4 30.0 2.1 2.5 5.0 — 3Fe 12 52.4 Extremely good none 17 53.7 28.0 1.4 1.9 — 10.0 5Fe 10 51.2 Extremely good none 18 49.3 32.0 1.5 2.2 10.0 — 5Ni 12 50.7 Extremely good none

TABLE 2 Thermal impact test (700° C.→quenching Impact wit water) Composition (mass %) value Hardness Overlay workability Presence or absence of No. Co Cr B Si W Mo Others J/cm² HRC State of molten pool cracks or exfoliation Comparative a 68.3 24.0 1.2 3.5 3.0 — — 22 44.8 Extremely good none Examples b 51.0 42.0 1.5 1.5 — 4.0 — 5 54.7 Extremely good present c 46.5 37.0 0.5 6.0 5.0 5.0 — 27 41.6 Good none d 57.8 30.0 2.7 2.5 7.0 — — 4 55.0 Extremely good present e 67.5 28.0 2.0 0.5 2.0 — — 13 46.9 Extremely good none f 63.6 32.0 1.4 3.0 — — — 19 46.1 Extremely good none g 52.8 30.0 2.2 2.0 5.0 8.0 — 7 51.3 Extremely good present h 55.2 26.0 1.5 2.3 — 5.0 10Ni 17 43.5 Extremely good none i 47.6 34.0 1.8 1.6 3.0 — 6Fe, 6Ni 18 45.3 Extremely good none j 52.7 38.0 0.8 3.0 2.5 2.5 0.5C 7 48.0 Good present

TABLE 3 Thermal impact test Overlay (700° C.→quenching Impact workability with water) Composition (mass %) value Hardness State of Presence or absence No. Co Mo W Cr B C Si Others J/cm² HRC molten pool of cracks or exfoliation Comparative A 65.7 — 4.6 28.5 — 1.2 — — 14 43.3 Good none Examples B 60.0 — 8.5 30.0 — 1.5 — — 6 48.4 Good present C 60.49 8.5 — 29.0 — 2.0 — 0.01Mn 7 48.2 Slightly poor present D 64.5 4.5 — 29.0 — 1.25 — 0.55Mn, 0.2Ti 15 42.1 Poor none E 58.2 12.0 — 28.0 — 0.3 — 1.5Ni 14 39.5 Slightly poor none F 59.7 29.0 — 8.5 — — 2.8 — 3 55.2 Poor present G 59.5 22.0 — 17.0 — 0.2 1.3 — 4 49.2 Slightly poor present H 56.4 27.0 — 14.0 — — 2.6 — 3 52.5 Slightly poor present I 60.32 28.5 — 8.5 — 0.08 2.6 — 2 51.6 Slightly poor present J 50.228 28.6 — 17.7 0.002 0.07 3.4 — 2 54.1 Poor present K 55.2 32.5 — 8.0 — 0.42 3.88 — 3 58.4 Slightly poor present L 59.23 28.7 — 9.3 0.02 0.19 2.56 — 4 51.9 Poor present M 38.68 40.1 — 19.1 — 0.02 2.1 — 1 x Poor present N 59.46 33.7 — 5.3 — 0.04 1.5 — 3 56.2 Slightly poor present O 59.798 21.4 — 16.6 — 0.0023 2.2 — 5 49.6 Slightly poor none P 40.6 6.0 — 18.5 3.4 — 3.5 28Ni 3 50.0 Extremely present good Q 66.8 — 8.0 20.0 2.7 — 2.5 — 4 57.0 Extremely none good ┌x┘ shows that the measurement could not be achieved since the alloy was fragile.

The alloys (a) to (j) of the Comparative Examples shown in Table 2 are alloys having a composition outside of the scope of the claims of the present invention. In the alloy (a), Co exceeds the upper limit of the claims, and Cr is below the lower limit. In the alloy (c), Co is below the lower limit of the claims, and Si exceeds the upper limit. In this case, the hardness is lowered. Also, in the alloy (e), Si is below the lower limit of the claims. The alloy (f) contains neither of W nor Mo. In the alloy (h), Ni exceeds the upper limit of the claims and, in the alloy (i), the sum amount of Fe and Ni exceeds the upper limit of the claims. In this case also, the hardness does not satisfy the target value. In the alloy (b), Cr exceeds the upper limit of the claims; in the alloy (d), B exceeds the upper limit; in the alloy (g), the sum of Mo and W exceeds the upper limit; and in the alloy (j), C exceeds the upper limit. In this case, the impact value does not satisfy the target value in any of these. In the Comparative Examples (b), (d), (g), and (j) in which the target of the Charpy impact value is not satisfied, generation of cracks was confirmed in the thermal impact test.

The alloys (A) to (Q) of the Comparative Examples shown in Table 3 are conventional Co—Cr—W—C type alloys (Stellite (registered trademark)), Co—Mo—Si type alloys (Tribaloy (registered trademark)), or alloys having a composition shown in other patent documents or self-fluxing alloy thermal spraying of JIS H 8303; however, none of these satisfies the target value of either the impact value or the hardness. Further, in the Comparative Examples (C) to (O), the overlay workability is poor. Also, in the Comparative Examples (B), (C), (F) to (N), and (P), generation of cracks was confirmed in the thermal impact test.

On the other hand, as shown in Table 1, the Examples 1 to 18 which are the alloys of the present invention satisfy the target values of all of the Charpy impact value, the Rockwell hardness, and the thermal impact test, and have a suitable hardness and a high toughness as a surface hardening material, and further are excellent in overlay workability.

INDUSTRIAL APPLICABILITY

As described above, the cobalt-based alloy provided by the present invention has excellent abrasion resistance and impact resistance properties as a surface hardening material, and also satisfies the fluidity property. Therefore, by forming such a material into a powder shape or a rod shape and performing surface hardening on various members by welding or thermal spraying, these members can be expected to enjoy a considerable improvement in durability.

Also, the cobalt-based alloy of the present invention is not limited to usage for filling, so that, by compositely adding this into a sintered component formed by powder metallurgy to form hard particles, this can be utilized also for forming a mechanical component having a good abrasion resistance.

DESCRIPTION OF REFERENCE SIGNS

-   -   1 engine valve     -   2 face surface (surface abutting against a sheet) 

1. A high-toughness cobalt-based alloy containing 25.0 to 40.0 mass % of Cr, 0.5 to 12.0 mass % of a sum of W and/or Mo, 0.8 to 5.5 mass % of Si, and 0.5 to 2.5 mass % of B, wherein the remainder comprises 48.0 to 68.0 mass % of Co and unavoidable impurities.
 2. The high-toughness cobalt-based alloy according to claim 1, further containing 8.0 mass°/or less of each of Fe, Ni, Mn, and Cu, and 0.3 mass % or less of C, wherein the sum amount of Fe, Ni, Mn, Cu, and C is 10.0 mass % or less.
 3. An engine valve filled or coated with a high-toughness cobalt-based alloy according to claim
 1. 4. The engine valve according to claim 3, wherein at least a face surface abutting against a sheet is filled or coated with said high-toughness cobalt-based alloy. 